ASME SA335-2013 pdf free download.SPECIFICATION FOR SEAMLESS FERRITIC ALLOY-STEEL PIPE FOR HIGH-TEMPERATURE SERVICE.
1.1 This specification covers nominal wall and mini- mum wall seamless frritic lloy-steel pipe intended for high-temperature service. Pipe ordered to this specification shall be suitable for bending, flanging (vanstoning), and similar forming operations, and for fusion welding. Selec- tion will depend upon design, service conditions, mechani- cal properties, and high-temperature characteristics.
1.2 Several grades of ferritic steels (see Note 1) are covered. Their compositions are given in Table 1. NOTE 1一Ferritie steels in this specification are defined as low- and intermediate- alloy steels containing u to and including 10% chromium.
1.3 Supplementary requirements (S1 to S7) of an optional nature are provided. These supplementary require- ments call for additional tests to be made, and when desired, shall be so stated in the order together with the number of such tests required.
1.4 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification. The inch-pound units shall apply unless the“M” designation of this specification is specified in the order. NOTE 2一The dimensionless designator NPS (nominal pipe size) has been substituted in this standard for such traditional terms as “nominal diameter,” “size,” and“nominal size.”
2. Referenced Documents
2.1 ASTM Standards: A 999/A 999M Specification for General Requirements for Alloy and Stainless Steel Pipe
E 213 Practice for Ultrasonic Examination of Metal Pipe and Tubing E 309 Practice for Eddy-Current Examination of Steel Tubular Products Using Magnetic Saturation E 381 Method of Macroetch Testing Steel Bars, Billets, Blooms, and Forgings E 527 Practice for Numbering Metals and Alloys in the Unified Numbering System (UNS) E 570 Practice for Flux Leakage Examination of Ferromag- netic Steel Tubular Products
2.2 ASME Standard: B36.10M Welded and Seamless Wrought Steel Pipe
2.3 Other Documents: SNT-TC-1A Recommended Practice for Nondestructive Personnel Qualfcation and Certification SAE J 1086 Practice for Numbering Metals and Alloys (UNS)
3. Ordering Information
3.1 Orders for material under this specification should include the following, as required, to describe the desired material adequately: 3.1.1 Quantity (feet, metres, or number of lengths), 3.1.2 Name of material (seamless aloy steel pipe), 3.1.3 Grade (Table 1), 3.1.4 Manufacture (hot-finished or cold-drawn), 3.1.5 Size using one of the following: 3.1.5.1 NPS and schedule number, 3.1.5.2 Outside diameter and nominal wall thickness, 3.1.5.3 Outside diameter and minimum wall thickness,3.1.5.4 Inside diameter and nominal wall thick- ness, and 3.1.5.5 Inside diameter and minimum wall thickness 3.1.6 Length (specific or random), 3.1.7 End finish (Ends Section of Specification A 999/A 999M)， 3.1.8 Optional requirements (Section 8, 12 and 13 of this specification. See the Sections on Hydrostatic Test Requirements and Permissible Variation in Weight for Seamless Pipe in Specification A 999/A 999M), 3.1.9 Test report required (Certification Section of Specification A 999/A 999M)， 3.1.10 Specification designation, and 3.1.11 Special requirements or any supplementary requirements selected, or both.
4.General Requirements
4.1 Material furmished to this specification shall con- form to the applicable requirements of the current edition of Specification A 999/A 999M, unless otherwise provided herein.
5. Materials and Manufacture 5.1 Pipe may be either hot finished or cold drawn with the finishing treatment as required in 5.3. 5.2 Grade P2 and P12一The steel shall be made by coarse- grain melting practice. Specific limits, if any, on grain size or deoxidation practice shall be a matter of agreement between the manufacturer and purchaser. 5.3 Heat Treatment: 5.3.1 All pipe shall be reheated for heat treatment and heat treated in accordance with the requirements of Table 2.ASME SA335 pdf download.